フィラメント物性表

※空欄は詳細データなし

名称
PLA
PLA(高速対応)
PLA Pro
MODERA:PLA
PLA Galaxy
PLAシルク
PLA木質
PLA Luminous
Green (蓄光)
ABS
ABS Pro
F.R. ABS
ESD-ABS
ABS Matte
ASA
PETG
PETG(高速対応)
ESD-PETG
TPU(95A)
PBAT
PA
PC
PLA-CF
PETG-CF
PVA
HIPS
PC-ABS
PBT-GF
プリント温度190~220℃190~240℃190~220℃200~230℃200~230℃200~230℃180~220℃190~220℃220~240℃220~240℃230-250℃220~240℃230~270°C240~260℃220~240℃220~260℃220~240℃170~220℃190~230℃220~260℃240~260℃190~220℃230~250℃190~220℃220~240℃250~280℃260-280℃
プリント速度60~90mm/s100~350mm/s60~90mm/s60~90mm/s60~90mm/s40~60mm/s60~90mm/s60~90mm/s60~90mm/s60~90mm/s——40~60mm/s40~250mm/s40~60mm/s60~90mm/s100~350mm/s40~60mm/s20~40mm/s30~60mm/s60~90mm/s60~90mm/s60~90mm/s60~90mm/s60~90mm/s60~90mm/s40~60mm/s——
プラットフォーム加熱50~60℃50~60℃50~60℃50~60℃50~60℃50~60℃50~60℃50~60℃80~110℃80~110℃100℃-120℃100℃80~110°C100~110℃80~100℃50~80℃80~100℃70~100℃50~60℃80~110℃100~120℃50~60℃70~90℃50~60℃80~110℃90~110℃100℃~120℃
密度1.25±0.05g/cm31.25~1.26g/cm31.25±0.05g/cm31.25±0.05g/cm31.25±0.05g/cm31.25±0.05g/cm31.20±0.05g/cm31.25±0.05g/cm31.04±0.2g/cm31.08±0.2g/cm31.19~1.20g/cm31.08~1.1g/cm31.04~1.06g/cm31.09±0.01g/cm31.27±0.05g/cm31.27~1.28g/cm31.27~1.28g/cm31.20±0.05g/cm31.25±0.05g/cm31.01±0.05g/cm3 1.20±0.05g/cm31.28±0.05g/cm31.28±0.05g/cm31.25±0.05g/cm31.04±0.2g/cm31.14~1.15g/cm31.32~1.35g/cm3
メルトフローレート
Melt Index MFR (190℃/2.16Kg)
ISO 1133
5~7g/10min10~20g/10min5~7g/10min5~10g/10min5~10g/10min3~5g/10min5~7g/10min5~7g/10min2~4g/10min2~4g/10min10~15g/10min8~12g/10min5~10g/10min3~4g/10min5~7g/10min 8~12g/10min 8~12g/10min2~4g/10min3~6g/10min5~7g/10min19~21g/10min(300℃,1.2Kg) 5~15g/10min5~15g/10min2~4g/10min2~5g/10min19~22g/10min15~20g/10min
吸水率(飽和,23℃)0.50%0.30%0.50%0.50%0.50%0.50%0.50%0.50%1%1%1%1%1%1.00%0.30%0.20%0.20%0.50%0.50%3.20%0.50%0.50%0.50%——1%<0.8%0.40%
引張強さ≥60MPa45~49Mpa≥50MPa≥60MPa≥60MPa≥60MPa≥40MPa≥60MPa≥43MPa≥53MPa30~35Mpa35~37Mpa35.5~36.5Mpa≥45Mpa≥52MPa41~45Mpa35~40MPa≥35MPa≥35MPa≥55MPa≥50MPa≥56MPa≥68MPa≥10MPa≥30MPa43.5~45.5MPa65~70Mpa
曲げ強さ≥60MPa70~80Mpa≥50MPa≥60MPa≥60MPa≥70MPa≥40MPa≥60MPa≥70MPa≥70MPa55~60Mpa60~61Mpa73.5~74.5Mpa≥65Mpa≥88MPa64~66Mpa64~66MPa≥35MPa≥35MPa≥58MPa≥89MPa≥98MPa≥15MPa≥60MPa71.5~74.5MPa100~110Mpa
曲げ弾性率≥2500MPa2000~2100Mpa≥2300MPa≥2500MPa≥2500MPa≥2500MPa——≥2500MPa≥2300MPa≥2300MPa1500~1650Mpa1300~1500Mpa 2070~2133Mpa≥2200MPa≥2200MPa1400~1500Mpa1400~1500MPa————≥1500MPa≥2200MPa≥2500MPa≥2700MPa≥190MPa≥1800MPa800~950MPa3700~4000Mpa
ノッチ衝擊強さ
IZOD,23℃
≥16J/m (ASTM D256)4.5~5KJ/㎡≥50J/m (ASTM D256)≥16J/m (ASTM D256)≥16J/m (ASTM D256)≥16J/m (ASTM D256)≥5J/m (ASTM D256)≥16J/m (ASTM D256)≥108J/m (ASTM D256)
≥19KJ/m2 (ISO179)
≥108J/m (ASTM D256)
≥19KJ/m2 (ISO179)
10~12KJ/㎡6~7KJ/㎡ 25.5~29.8 KJ/㎡(ISO180)≥14KJ/m2 (ISO179)——5~6KJ/㎡5~6KJ/㎡————≥16KJ/m2 (ISO179)≥700J/m (ASTM D256)≥30J/m(ASTM D256)——≥16J/m (ASTM D256)≥100J/m (ASTM D256)43.5~44.5KJ/㎡2~3KJ/㎡
破断伸び率≥3.0%10.5~15.5%≥10%≥3.0%≥3.0%≥10%≥2.0%≥3.0%≥30.0%≥30.0%8~10%5~7% 5~6.5%——≥150.0%10~12%5~8%≥700.0%≥350.0%≥200.0%≥50.0%≥2%≥50%≥11.0%≥50.0%24~26%2~3%
熱変形温度≥53℃≥53℃≥53℃≥53℃≥53℃≥55℃≥50℃≥53℃≥88℃≥88℃≥88℃≥98℃≥88℃≥80℃≥70℃≥68℃≥65℃——≥90℃≥85℃≥125℃≥55℃≥70℃≥55℃≥90℃≥123℃≥175℃
直径1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm1.75mm
公差±0.05mm——±0.05mm±0.05mm±0.05mm±0.05mm±0.05mm±0.05mm±0.05mm±0.05mm——————±0.05mm±0.05mm————±0.05mm±0.05mm±0.05mm±0.05mm±0.05mm±0.05mm±0.08mm±0.05mm-0.01mm——
円度——————————————————————————————————————————————————————
造形物の表面抵抗——————————————————————10^5~10^7Ω————————10^5~10^7Ω————————————————————
造形物の比誘電率——————————————————————————————————————————————————————
造形物の誘電正接——————————————————————————————————————————————————————
造形物の磁性——————————————————————〇(極微、実測値は不明)————————〇(極微、実測値は不明)————————————————————